Electrochemical Behaviors of the Loaded Stainless Steel in Dilute Thiosulphate Solution

Authors

Changjian Lin, State Key Laboratory for Physical Chemistry of the Solid Surface Department.of Chemistry ,Xiamen University ,Xiamen 361005;
Zude Feng, State Key Laboratory for Physical Chemistry of the Solid Surface Department.of Chemistry ,Xiamen University ,Xiamen 361005;
Fuling Lin, State Key Laboratory for Physical Chemistry of the Solid Surface Department.of Chemistry ,Xiamen University ,Xiamen 361005;
Fayang Wang, State Key Laboratory for Physical Chemistry of the Solid Surface Department.of Chemistry ,Xiamen University ,Xiamen 361005;
Jianguang Tang, State Key Laboratory for Physical Chemistry of the Solid Surface Department.of Chemistry ,Xiamen University ,Xiamen 361005;
Yuanhui Wang, State Key Laboratory for Physical Chemistry of the Solid Surface Department.of Chemistry ,Xiamen University ,Xiamen 361005;

Abstract

The electrochemical behavior of l8/8 stainless steel in dilute thiosulphate solutionduring strained loading was studied by various electrochemical techniques and scanning electronmicroscope.It is evidenced that the corrosion activity of stainless steel increased with strained loading.The dynamic process of repassivation ,which may datermine the initiation ,the cease and developmentof the stress corrosion cracking for stainless steel ,was strongly influenced by both electrochemical andloading conditions. Pitting corrosion may locate preferentially on the sites which was suffered mostloading.The propagation of pitting corrosion of stainless steel may induce stress corrosion crakingunder certain conditions.

Keywords

Stainless steel, Stress corrosion cracking, Electrochemical behavior

DOI Link

https://doi.org/10.61558/2993-074X.1317

Publication Date

1995-11-28

Online Available Date

1995-11-28

Revised Date

1995-11-28

Received Date

1995-11-28

Recommended Citation

Changjian Lin, Zude Feng, Fuling Lin, Fayang Wang, Jianguang Tang, Yuanhui Wang. Electrochemical Behaviors of the Loaded Stainless Steel in Dilute Thiosulphate Solution[J]. Journal of Electrochemistry, 1995 , 1(4): 439-445.
DOI: 10.61558/2993-074X.1317
Available at: https://jelectrochem.xmu.edu.cn/journal/vol1/iss4/10

References

l肖纪美．不锈钢的金属学问题．北京：冶金工业出版社，19832NewmanRC．ElectrochemicalandopticalTechniquesforthestudyandMonitoeingofMetallicCorrosion．FerreiraMGS，MelendresCAeds．1991：5853CragnolinoG，MaedonaldDD．Intergranularstresscorrcoioncrakingofausteniticstainlesssteelattemperaturesbelow100℃－Areview．Corrosion，1982，38：4064IsaacsHH．Initiationofstresscorrosioncrackingofsensitizedtype304stainlesssteelindilutethiosulfatesolution．J．Electrochem．Soc．，1988，135：21805WellsDB，StewartJ，DavidsonRetal．Themechanismofintergranularstresscorrosioncrackingofsensitisedausteniticstainlesssteelindilutethisulphatesolution．CorrosionScience，1992，33：396金石（译）．金属力学化学与腐蚀防护．北京：科学出版社，19897ZhangXG，VereeckenJ．RepassivationandstresscorrosioncrackingofΓi－6Al－4Vinaqueousandmethanolicsolution。Corrosion．1989，45：578田昭武等．电化学实验方法进展．厦门：厦门大学出版社，19889乔利杰，肖纪美，林昌健．黄铜应力腐蚀开裂的电位前驱效应．中国腐蚀与防护学报，1991，11：61