Study on the Corrosion of Chlorine Condenser by Electrochemical Method

Authors

Bin XIANG, College of Chemistry & Chemical Engineering,Chongqing University,Chongqing 400044,China,;
Wen CHEN, College of Chemistry & Chemical Engineering,Chongqing University,Chongqing 400044,China,;
Wen-zhang HUANG, Chongqing University of Science & Technology,Chongqing University,Chongqing 40001,China;
Shao-hua XING, College of Chemistry & Chemical Engineering,Chongqing University,Chongqing 400044,China,;
Sheng-tao ZHANG, College of Chemistry & Chemical Engineering,Chongqing University,Chongqing 400044,China,;

Abstract

Corrosion of condenser is very seriously in chlorine-alkali industry,which could lead to fatal disaster.The most commonly used material in low pressure condenser includes steel of 16MnR,10#,and welding rod of J507.Electrochemical analysis of the three materials in 29.9%(by mass) calcium chloride(CaCl2) solution was carried out.The corrosion current density icorr and impedance parameters of the three materials in 29.9% CaCl2 solution were estimated separately.The result showed that in the tripartite phase regions where the 10# seamless tube and 16MnR armor plate were jointed by welding,the weld was firstly eroded and suggested that the chlorine condenser should be examined and repaired every year.

Keywords

condenser, chlorine, linear polarization, salt bath, EIS

DOI Link

https://doi.org/10.61558/2993-074X.1844

Publication Date

2007-11-28

Online Available Date

2007-11-28

Revised Date

2007-11-28

Received Date

2007-11-28

Recommended Citation

Bin XIANG, Wen CHEN, Wen-zhang HUANG, Shao-hua XING, Sheng-tao ZHANG. Study on the Corrosion of Chlorine Condenser by Electrochemical Method[J]. Journal of Electrochemistry, 2007 , 13(4): 411-414.
DOI: 10.61558/2993-074X.1844
Available at: https://jelectrochem.xmu.edu.cn/journal/vol13/iss4/11

References

[1]Hu Dongsheng(胡东升).Reason analysis and controlmeasure of chlorine condenser corrosion perforation[J].Journal of Suzhou University(in Chinese),2002,5:22.
[2]Zhang Yuansheng(张远声).Corrosion destroyed acci-dent[M].Beijing:Chemical Industry Press,2000.
[3]Zhang Jintao,Hu Jiming,Zhang Jianqing,et al.Stud-ies of water transport behavior and impedance models ofepoxy-coated metals in NaCl solution By EIS[J].Pro-gress in Organic Coatings,2004,51:145-151.
[4]Cao Chunan(曹楚南).Principles of corrosion electro-chemistry[M].Beijing:Chemical Industry Press,2004.
[5]Xiang Bin(向斌),Xing Shaohua(邢少华),ZhangShengtao(张胜涛).Study the corrosion of chlorine con-denser by ICT[J].Corrosion Science and ProtectionTechnology,2005:5:352.
[6]Hemmingsen T,Hovdan H,Sanni P,et al.The influ-ence of electrolyte reduction potential on weld corrosion[J].Electrochimica Acta,2004,47:3949-3955.