Study of Black Electromagnetic Shielding Fabric

Authors

Shao-wen LU, Key Laboratory of Science & Technology of Eco-textile,Ministry of Education,College of Chemistry andChemical Engineering,Donghua University,Shanghai 201620,China;
Wei WANG, Key Laboratory of Science & Technology of Eco-textile,Ministry of Education,College of Chemistry andChemical Engineering,Donghua University,Shanghai 201620,China;
Bin SUN, State Key Laboratory for Modificationof Chemical Fibers and Polymeric Materials,College of Material Science and Engineering,Donghua Univ.,Shanghai 201620,China;

Abstract

A soft electromagnetic shielding fabric was successfully prepared by electroplating black nickel on the Cu-plated PET fabric,preliminary thechnigue conditions were carried out as NiSO4·6H2O 40 g·L-1,H3BO3 30 g·L-1,NiSO4·(NH4)SO4·6H2O 40 g·L-1,ZnSO4·7H2O 50 g·L-1,NH4CNS 20 g·L-1,pH=4,t=30℃.The expericments showed that the soft electromagnetic shielding fabric had good conductive and electromagnetic shielding effectiveness,great abrasion resistance and erosion resistance performance and excellent absorbency performance,all of these promote the fabric decoration,protection and absorbency property.

Keywords

electroplate black nickel, electromagnetic shielding fabric, abrasion resistance, erosion resistance, absorbency

DOI Link

https://doi.org/10.61558/2993-074X.1862

Publication Date

2008-02-28

Online Available Date

2008-02-28

Revised Date

2008-02-28

Received Date

2008-02-28

Recommended Citation

Shao-wen LU, Wei WANG, Bin SUN. Study of Black Electromagnetic Shielding Fabric[J]. Journal of Electrochemistry, 2008 , 14(1): 51-55.
DOI: 10.61558/2993-074X.1862
Available at: https://jelectrochem.xmu.edu.cn/journal/vol14/iss1/11

References

[1]Abis S,Lorenzetti ML.An analysis of black-nickel re-sistance to a humid environment[J].Journal of Materi-als Science Letters,1985,4(1985):1102-1107.
[2]HUWen-xu(胡文旭),LUBai-zuo(鲁百佐).Study inoptical property of black-nickel selectively absorbingcoat[J].Journal of Shaanxi Normal University(NaturalScience Edition)(in Chinese),2002,30(4):61-63.
[3]HU Wen-xu(胡文旭).Study of the black-nickel coat-ing preparation and its optical proerty[J].Acta Enger-giae Solaris Sinica,2001,22(4):443-447.
[4]Abis S.The structure and optical response of a nickelblack selective coating[J].Journal of Materials Sci-ence,1987,22(1987):219-222.
[5]Robert W Farrell.Blackening of ferrous metals[J].Metal Finishing,2002,1(100):456-462
[6]Magdy A M.Black nickel electrodeposition from a mod-ified Watts bath[J].Journal of Applied Electrochemis-try,2005,36:295-301.
[7]ZHAO Fu-chen(赵福辰).Development of electromag-netic shielding materials[J].Development and Applica-tion of Materials(in Chinese),2001,16(5):29-33.
[8]SHANG Si-shan(商思善).The fabric of the chemicalcopper-nickel duplicate coating[J].Technical Textiles(in Chinese),2002,20(143):44-45.
[9]LI Di(李荻),GUO Bao-lan(郭宝兰),LI Hong(李宏).Metal/fabric composite material for EMI/RFIshielding[J].Acta Aeronautica Et-Astronautica Sinica(in Chinese),2000,21(Sup):43-47.
[10]Vishal Saxena,Uma Rani R,Sharma A K.Studies onultra high solar absorber black electroless nickel coat-ings on aluminum alloys for space application[J].Sur-face&Coatings Technology,2006,(201):855-862.
[11]LI Cheng-hong(李成虹).Analysis of black nickelplating bath[J].Plating and Finishing(in Chinese),2004,26(3):36-37.
[12]ZHANG Sheng-tao(张胜涛).The project of eletro-plating[M].Beijing:Chemical Industry Press,2005.161-163.