Abstract
The influence of electrolytic composition on the interfacial electric Characteristic of the porous membrane membrance of anodized aluminum was investigated with a electrodialytic method. Results indicated that, when the porous membrane was pretreated with F -, PO 3- 4,SiO 2- 3 and tannic acid, the isoelectric point in 0.01 mol/L KCI, were shifted from normal 9.20 to 3.40, 4.30, 3.30 and 4.50, respectively, and responsive characteristics of ζ potential to pH was changed. Furthermore, after pretreatment of porous membrance with fuchsine basic and fuchsine acid solution,there was no isoelectric point at 2.0
Publication Date
1998-08-28
Online Available Date
1998-08-28
Revised Date
1998-08-28
Received Date
1998-08-28
Recommended Citation
Yafe Kuang, Ling Wang, Meiyuan Wang.
Influence of Electrolytes to the Interfacial Electroc Characteristics of the Porous Membrane of Anodized Aluminum[J]. Journal of Electrochemistry,
1998
,
4(3): Article 8.
DOI: 10.61558/2993-074X.2702
Available at:
https://jelectrochem.xmu.edu.cn/journal/vol4/iss3/8
References
1多田隈昭．阳极酸化皮膜の逆电はく离法．实务表面技术，1986，33（7）：254～2582旷亚非，王玲，胡飞．铝阳极氧化多孔膜层的界面电性能研究．电化学，1998，4（2）：164～1693佐藤敏彦著，既调和，董建中，梁启民译．铝阳极氧化理论100题问答．天津：天津科技翻译出版公司，1989：10～204ShortEP，MoritaA．Themechanismofcoldsealing．PlatingandSurfaceFinshing，1988，95：102～1075KalantaryMR，GabeDR，RosDH．Amodelforthemechanismofnickelfluoridecoldsealingofanodizedaluminum．J．Appl．Electrochem，1992，22：268～2766DitoA，TegiacciF．Coldsealingofanodizedaluminumwithnickelsaltsolution，PlatingandMetalFinshing，1985，72（6）：72～787SkeldonP，ShimizvK，ThompsonGE，WoodGC．Selectiveinterfacialprocessestheincorporationofelectrolytespeciesintoanodicfilmonaluminum．PhilosophicalmagazineB，1995，72（4）：391～4008黑田孝一，阳极酸化皮膜の着色．表面技术，1995，46（5）：4154199既调和，曾凌三，张国芝．建筑铝型材的阳极氧化和电解着色．长沙：湖南科学技术出版社，1994：132～134