Abstract
The spinel Li intercalation compound Li 1+ x Mn 2- x O 4(0< x <1) was prepared by using techniques of cyclic voltammetry. The electrochemical parameters of Li 1+ x Mn 2- x O 4 electrode vary as either the starting materials or the synthesis temperature changes. It was found that the initial capacity and reversible behaviors of the Li 1+ x Mn 2- x O 4 electrode depends on the amount of the excess Li, represented as x in Li 1+ x Mn 2- x O 4. The reversible of Li intercalation process for Li 1+ x Mn 2- x O 4 electrode was demonstrate by cyclic voltammograms.
Keywords
Lithium on battery, Spinel, Initial capacity
Publication Date
1998-11-28
Online Available Date
1998-11-28
Revised Date
1998-11-28
Received Date
1998-11-28
Recommended Citation
Xiaomei Wu, Qinghe Yang, Zhongkao Jin, Haoqing Wu, Xiangfu Zong.
Studies of Spinal Li 1+x Mn 2-x O 4 Rechargeable Lithium Ion Battery[J]. Journal of Electrochemistry,
1998
,
4(4): Article 9.
DOI: 10.61558/2993-074X.3144
Available at:
https://jelectrochem.xmu.edu.cn/journal/vol4/iss4/9
References
1YongyaoXia．AnInvestigationofIonInsertionintoSpinelStructureLiMnOCompounds．J．Electrochem．Soc．，1996，143：8252Momchilov．A．RechargeablelithiumbaterywithspinelrelatedMnO2．J．PowerSources，1993，41：305～314．3Pistoia．G．SomeaspectsofLiMn2O4electrochemistryinthe4voltrange．1995，142：2551．4YuanGao．ChangesinthevoltageprofileofLi／Li1＋xMn2－xO4celasafunctionofx．TheAmericanPhysicalSociety，1996，54：3878．5TsutomuOhzuku．ElectrochemistryofManganeseDioxideinLithiumNonaqueousCels．J．Electrochem．Soc．，1991，138：2556．
Included in
Engineering Science and Materials Commons, Materials Chemistry Commons, Materials Science and Engineering Commons, Physical Chemistry Commons, Power and Energy Commons