Abstract
Al and Li elements were co_doped into host spinel lithium manganese oxide by a simple and economical preparation technology . There was an investigation of the influence of doped Al contents on the initial capacity and cycling performance of the materials. The investigation of the XRD patterns, the analysis of the SEM micrographs and the determination of IR spectroscopy showed that the particles of dopant materials are fine, narrowly distributed and well crystallized, and the bonds Mn_O are stronger than these of undoped materials. The resulted materials have a high initial capacity of 119 mAh/g and good cycling characterization. The capacity still kept at 106 mAh/g after 200 cycles.
Keywords
Lithium_ion batteries, LiMn 2O 4, Cation dopant, IR spectroscopy
Publication Date
2001-11-28
Online Available Date
2001-11-28
Revised Date
2001-11-28
Received Date
2001-11-28
Recommended Citation
Zi-shan ZHENG, Zi-long TANG, Zhong-tai ZHANG, Wan-ci SHENG.
An Investigation of Structural Properties of Li-Al-mixed Doped Spinels Materials Li_(1+x) Al_yMn_(2-y)O_4[J]. Journal of Electrochemistry,
2001
,
7(4): Article 14.
DOI: 10.61558/2993-074X.3269
Available at:
https://jelectrochem.xmu.edu.cn/journal/vol7/iss4/14
References
[1] XiaYongyao,ZhouYunhong,YoshioMasakiCapacityfadingoncyclingof4VLi/LiMn2O4[J].J.Elec trochem.Soc.,1997,144:2593～2600.
[2] GummowRJ ,KockAde,ThackerayMM .Improvedcapacityretentioninrechargeable4Vlithiumman ganeseoxide(spinel)cells[J].SolidstateIonics,1994,69:59～67.
[3] ThackerayMM ,Shao～HornY ,KahaianAJ .Structuralfatigueinspinelelectrodesinhighvoltage(4V)Li/LixMn2O4 cells[J].ElectrochemSolidStateLett.,1998,1:7～8.
[4] LeeJongH ,HongJinK ,JangDongH ,etal.DegradationmechanismsindopedspinelsofLiM0.05Mn1.95O4(M =Li,B ,Al,Co,andNi)forLisecondarybatteries[J].J .PowerSources,2000,89:7～14.
[5] AroraP ,PopovBN ,WhiteRE .Electrochemicalinvestigationsofcabalt_dopedLiMn2O4 ascathodematerialforlithium_ionbatteries[J].J .Electrochem.,Soc.,1998145:807～814.
[6] TarasconJM ,MckinnonWR ,CoowarF ,etal.SynthesisconditionsandoxygenstoichiometryeffectsonLiinsertionintothespinelLiMn2O4[J].J .Electrochem.Soc.,1994,141:1424～1431.
[7] VoglerC ,ButzA ,DittrichH ,etal.Electrochemicalandstructuralcomparisonofdopedlithiummanganesespinels[J].J.PowerSources1999,84:243～247.
[8] TarasconJM ,WangE ,ShokoohiF ,K .ThespinelphaseofLiMn2O4 asacathodeinsecondarylithiumcells[J].J .Electrochem.Soc.,1991,138:2859～2864.
[9] RobertsonAD ,LuSH ,HowardWF .M3+_modifiedLiMn2O4 spinelintercalationcathodesⅡElectro chemicalstabilizationbyCr3+[J].J .Electrochem.Soc.,1997,144:3500～3512.
[10] Wohifahrt_MehrensM ,ButzA ,OestenR .Theinfluenceofdopingontheoperationoflithiummanganeseoxidespinel[J].J.Electrochem.Soc.,1997,68:582～585.
[11] LiGuohua,IkutaH ,VchidaT ,WakiharaM .ThespinelphasesLiMyMn2yO4(M =Co,Cr,Ni)asthecath odeforrechargeablelithiumbatteries[J].J.Electrochem.Soc.,1996,143:178～182.
[12] AroraP .PopovBN ,WhiteRE .Electrochmicalinvestigatonsofcobalt_dopedLiMn2O4 ascathodematerialforlithium_ionbatteries[J].J .Electrochem.Soc.,1998,145:807～815.
[13] PereamuageD ,AbrahamKM .PreparationandelectrochemicalcharacterizationofoverlithiatedspinelLiMn2O4[J].J .Electrochem.Soc.,1998,145:1131～1136.
[14] WangGX ,BradhurstDH ,LiuHK ,etal.ImprovementofelectrochemicalpropertiesofthespinelLiMn2O4 usingaCrdopanteffect[J].SolidStateInics,1999,120:95～101.
[15] SongD ,IkutaH ,UchidaT ,WakiharaM .ThespinelphasesLiAlyMn2_yO4(y=0,1/12,1/9,1/6,1/3)andLi(Al,M )1/6Mn11/6O4(M =Cr,Co)asthecathodeforrechargeablelithiumbatteries[J].SolidStateInics,1999,117:151～156.
[16] OhzukuT ,KitagawaM ,HiraiT .ElectrochemistryofmanganesedioxideinlithiumnonaqueouscellⅢ.X_raydiffractionalstudyonthereductionofspinel_relatedmanganes4edioxide[J].E .J .Electrochem.Soc.,1990,137:769～775
Included in
Engineering Science and Materials Commons, Materials Chemistry Commons, Materials Science and Engineering Commons, Physical Chemistry Commons, Power and Energy Commons