The Electrophoretic Deposition of Nano Hydroxyapatite Coating on Titanium Surface

Authors

Fei CHEN, *1),WANG Zhou-cheng~2(1.State Key Lab for Physical Chemistry of Solid Surfaces,Department of Chemistry, Xiamen University, Xiamen 361005, China,2.Department of Materials Science and Engineering, Xiamen University, Xiamen~()361005, China;
Chang-jian LIN, *1),WANG Zhou-cheng~2(1.State Key Lab for Physical Chemistry of Solid Surfaces,Department of Chemistry, Xiamen University, Xiamen 361005, China,2.Department of Materials Science and Engineering, Xiamen University, Xiamen~()361005, China;

Abstract

A hydroxyapatite coating with nano-structure on the roughened titanium surface was prepared by electrophoretic deposition process. To decrease sintering temperature the HAp nanoparticles synthesizedby a wet chemical method was used. It is observed that the coating is uniform without cracks. After sintering the nano-strueture of HAp coating remains unchanged. The surface treatment of Ti is applied to form a distribution of small pits and TiO_2thin layer that improve the adhesion of coatingto Ti substrate. It is shown that the bonding strength of coating is as high as 18±2.5MPa. The hardness and Young's modulus are 40.6 and 0.42 GPa, respectively.

Keywords

Hydroxyapatite, Nano coating, Electrophoretic deposition

DOI Link

https://doi.org/10.61558/2993-074X.1616

Publication Date

2005-02-28

Online Available Date

2005-02-28

Revised Date

2005-02-28

Received Date

2005-02-28

Recommended Citation

Fei CHEN, Chang-jian LIN. The Electrophoretic Deposition of Nano Hydroxyapatite Coating on Titanium Surface[J]. Journal of Electrochemistry, 2005 , 11(1): 67-71.
DOI: 10.61558/2993-074X.1616
Available at: https://jelectrochem.xmu.edu.cn/journal/vol11/iss1/13

References

[1]　JiH,MarquisPM.Effectofheattreatmentonthemi crostructureofplasma sprayedhydroxyapatitecoating[J].Biomaterials,1993,14:64.
[2]　BanS,MarunoS.Effectoftemperatureonelectrochem icaldepositionofcalciumphosphatecoatingsinasimu latedbodyfluid[J].Biomaterials,1995,16:977.
[3]　ChaiCS,BenNissanB.Bioactivenanocrystallinesol gelhydroxyapatitecoatings[J].J.MaterSci:MaterMed.,1999,10:465.
[4]　YankeeSJ,PletkaBJ,LuckeyHA, etal.Processesforfabricatinghydroxyapatitecoatingsforbiomedicalap plications, thermalsprayresearchandapplication[A].ProceedingsoftheThirdNationalThermalSprayConfer ence[C].California:LongBeach,1990.433.
[5]　KnowlesJC,GrossK,BerndeCC, etal.Structuralchangesofthermallysprayedhydroxyapatiteinvestigatedbyrietveldanalysis[J].Biomaterials,1996,17:639.
[6]　MaoC,LiH,CuiF, etal.Orientedgrowthofphos phatesonpolycrystallinetitaniuminaprocessmimic kingbiomineralization[J].J.CrystalGrowth,1999,206:308.
[7]　SridharTM,MudaliUK,SubbaiyanM.Preparationandcharacterizationofelectrophoreticallydepositedhydroxyapatitecoatingsontype316Lstainlesssteel[J].CorrosionScience,2003,45:237.
[8]　DeSenaLA,DeAndradeMC,RossiAM, etal.Hydroxyapatitedepositionbyelectrophoresisontitaniumsheetswithdifferentsurfacefinishing[J].J.BiomedMaterRes.,2002,60:1.
[9]　SarkarP,NicholsonPS.Electrophoreticdeposition(EPD): mechanisms[J].Kinetics, andApplicationtoCeramics,J.Am.Ceram.Soc.,1996,79(8):1987.
[10]　YeongKCB,WangJ,NgSC.MechanochemicalsynthesisofnanocrystallinehydroxyapatitefromCaOandCaHPO4[J].Biomaterials,2001,22:2705.
[11]　KongLB,MaJ,BoeyF.Nanosizedhydroxyapatitepowdersderivedfromcoprecipitationprocess[J].J.Mater.Sci.,2002,37:1131.
[12]　NarasarajuTSB,PhebeDE.Review: somephysico chemicalaspectsofhydroxylapatite[J].J.MaterialsScience,1996,31:1.
[13]　MalzbenderJ,WithGde.Theuseoftheloadingcurvetoassesssoftcoatings[J].SurfaceandCoatingsTechnology,2000,127:266.
[14]　JaeYoungRho,PharrGM.Effectsofdryingonthemechanicalpropertiesofbovinefemurmeasuredbynanoindentation[J].J.Mater.Sci:Mater.Med.,1999,10:485.
[15]　RoopKumar,M.Wang.Functionallygradedbioactivecoatingsofhydroxyapatite/titaniumoxidecompositesystem[J].MaterialsLetters,2002,55:133.
[16]　WeiM,RuysJ,SwainMV, etal.Interfacialbondstrengthofelectrophoreticallydepositedhydroxyapatitecoatingsonmetals[J].J.MaterSci.MaterMed,1999,10:401.