Abstract
The nano diamond stable water disperse system was studied.The low-bublles sulfonic anion sufcace active agent had been choosed out for this system.The affect of different physics agitation mothed on the water separate system stablity were conpared.The nano diamond stable water separate system had been applied to the composite chromium electroplating on this tests.The depositing speed,hardnees and wearing capacity of plating layer were tested.And the metallography structure of plating layer was charasterized by SEM.The test results and reaction princeple were discussed.
Keywords
nano-diamond, composite chromium plating, water separate system
Publication Date
2007-08-28
Online Available Date
2007-08-28
Revised Date
2007-08-28
Received Date
2007-08-28
Recommended Citation
Lai-xiang ZHANG, Hong-bo XIE, Xue-kui MA, Guo-wu ZHAO, En-cheng YU, Jia-zhi WANG.
Study on the Nano Diamond Stable Water Disperse System and Applying in Composite Chromium Plating[J]. Journal of Electrochemistry,
2007
,
13(3): 288-292.
DOI: 10.61558/2993-074X.1824
Available at:
https://jelectrochem.xmu.edu.cn/journal/vol13/iss3/12
References
[1]ZHU Yong-wei(朱永伟),WANG Bo-chun(王柏春),CHEN Li-fang(陈立舫).The application actaulity andforeground of nano diamond[J].Material LeadingNewspaper(in Chinese),2002,116(12):27-30.
[2]ZHANG wei-da(张书达).The apllication of nano dia-mond[J].Industry Diamond(in Chinese),2001,3:6-7.
[3]YU Jie(于杰),LIU Jian-ping(刘建平),ZHAO Gou-ping(赵国鹏).The preparation of the SiO2water sepa-rate system and application on electroplating[J].Plat-ing and Surface Finishing(in Chinese),2003,23(2):25-26.
[4]YANG Dong-qing(杨冬青),ZHANG Hua-tang(张华堂),TONG Xiao-hui(佟晓辉).The tribology capabil-ity on the nano diamond composite chromium electropla-ting layer[J].Metal Heating Treatment(in Chinese),2001,27(6):5-7.