Abstract
Using KH-550 as precursors,gel thin films were formed on fabric by sol-gel method.By complexed with palladium ions due to the presences of amido and hydroxide in the gel thin films,the aggregation of palladium particles was inhibited.Therefore,Palladium could exhibit better catalytic activity in the process of electroless plating.The surface morphology of fabric was observed by SPM and SEM.Campared with the traditional pretreatment process,no SnCl2 was needed.This method reduced pollution,shortened process flow and reduced the amount of noble metals.
Keywords
KH-550, sol-gel, electroless plating, nylon fabric, Pd
Publication Date
2010-02-28
Online Available Date
2010-02-28
Revised Date
2010-02-28
Received Date
2010-02-28
Recommended Citation
Lin ZHANG, Wei WANG, Qian-zhen Wu.
Application of Sol-Gel Technology in the of Activation Process of Chemical Plating Pretreatment[J]. Journal of Electrochemistry,
2010
,
16(1): 112-115.
DOI: 10.61558/2993-074X.2049
Available at:
https://jelectrochem.xmu.edu.cn/journal/vol16/iss1/23
References
[1]Eun Gyeong Han,Eun Ae Kim,Kyung Wha Oh.Electro-magnetic interference shielding effectiveness of electro-less Cu-plated PET fabrics[J].Synthetic Metals,2001,123:469-476.
[2]Zhan Jianchao(詹建朝),Zhang Hui(张辉),Shen Lan-ping(沈兰萍).Study on the different increasing weight rate of electroless nickel plating on PET fabric[J].Technical Textiles,2006(产品用纺织品),8:26-29.
[3]Textor T,Bahner T,Schollmeyer E,et al.Surface modifi-cation of textile fabrics by coatings based on the sol-gel process[J].Melliand Textiber,1999(10):E229.
[4]XU Peng(徐鹏),WANG Xiao-wen(王晓文),CHEN Shui-lin(陈水林),et al.Improving the antistatic prop-erty of polyester fabric by sol-gel process[J].Dyeing&Finishing(印染),2005,21:4-6.
[5]Wang Lejun(王乐军),Ding Zhaotao(丁兆涛),LüCui-lian(吕翠莲),et al.Development of Antiradiation Fab-ric and Garment[J].Technical Textiles(产业用纺织品),2002,20(10):12-14.