Hydrogen Evolution Reaction on Nanocrystalline Co-Mo/Ni Composite-Coated Electrodes

Authors

Weizeng Yu, Department of Chemistry, Capital Mormal University, Beijing 100037;
Jie Ma, Department of Chemistry, Capital Mormal University, Beijing 100037;
Yiming Chu, Department of Chemistry, Capital Mormal University, Beijing 100037;
Huizhe Zhu, Department of Chemistry, Capital Mormal University, Beijing 100037;
Hongjie Wang, Department of Chemistry, Capital Mormal University, Beijing 100037;
Shuncheng Liu, Department of Chemistry, Capital Mormal University, Beijing 100037;

Abstract

The electrochemical behaviours of the hydrogen evolution reaction(HER) at electrodes prepared by composite coating of nanocrytstalline Co-Mo alloy particles formed by ball milling on nickel base has been sludied by using sleady-state polarization and ac impedance techiu ques.The microstructure and the size of the nanocrystals of Co- Mo alloy and the morphology of the composite-coating surface of the electrodes are measured by XRD, TEM and SEM. Results show that the nanocrystalline Co-Mo alloys prepared by high energy ball milling has high electrocatalytic activity for HER. The electrocatalytic activity for the HER is enhanced and the energy of activation for HER is decreased with increasing milling time. They are attributed to the increase in the real surface areas of the electrode and high proportion of active atoms on the surface of electrodes. The temperature study show that the energy of activation of electrodesorption is the same as the energy of activation of the overall reaction. The reaction rate of HER on the electrodes is proved to be controlled by electrodesorption.

Keywords

Hydrogen evolution reaction, Nanocrystalline, Co-Mo alloy, Thmposite coating, Bali milling

DOI Link

https://doi.org/10.61558/2993-074X.3053

Publication Date

1996-02-28

Online Available Date

1996-02-28

Revised Date

1996-02-28

Received Date

1996-02-28

Recommended Citation

Weizeng Yu, Jie Ma, Yiming Chu, Huizhe Zhu, Hongjie Wang, Shuncheng Liu. Hydrogen Evolution Reaction on Nanocrystalline Co-Mo/Ni Composite-Coated Electrodes[J]. Journal of Electrochemistry, 1996 , 2(1): Article 12.
DOI: 10.61558/2993-074X.3053
Available at: https://jelectrochem.xmu.edu.cn/journal/vol2/iss1/12

References

1杨军，紫亮，邓景发等．非晶态合金作催化材料的研究．化学学报，1994，52（1）：532FanY，HuZhang，ShnJetal．，SurfacestateandcatalyticactivityofultrafinceamorphousNiBalloyparticlespreparedbychemicalreduction．J．Mater．Sci．Lett．，1993，12：596～5973HuotJY，TrudeauML，SchulzR．LoWhydrogenoverpotentialnanoerystallineNi－Mocathaesforalhalinewaterelectrolvsis．J．Electrochem．Sor．，1991，138：1317～13214YamashitaHiroya，YamamuraTakeshi，YoshimotoKatsutoshi．Therelationbetweencatalyticabllityforhydrogenevolutionreactionandcharacteristicsofnickel－tinalloys．J．ElectrochemSor．，1993，140：2238～22435马洁，蒋雄，江琳才等．球磨形成的Ni－Mo纳米晶复合镀层上的析氢反应．物理化学学报（待发表）6FanChonglun，PlronDL，SlebAbderrahmanetal．Studyofelertrodepositednickel－molybdenum，nickel－tungsten，cohaltmolybdenumandcohalttungstenashydrogenelectrodesinalhalinewaterelectrolysis．J．Electrochem．Sor．，1994，141：382～3877ArmstrongRD．HendersonMImpedanceplanedisplayofareactionwithanadsorbedintermediate．J．Electroanal．Chem．，1972，39：81～908OkidoM，DepoIK，CapuanoGAThemechanismofhydrogenevolutionreactiononamodifiedRaneynickelcompeite－coatedelectrodebyacimpedance．J．Electrochem．Sor．，1993，140：127～1339DcGizMJ，FerreiraG，Tremilliosi－FilhoGetal．MechanisticstudyofthehydrogenevolutionreactiononNi－ZnandNi－Scathodes．J．Appl．Electrochem．，1993，23：641～64510OhmsD，PlzakV，TrasattiSetal．ElectrochemicalHydrogenTechnolohies．ElectrochemicalProductionandCombustionofHydrogen．Amsterdam：HartmutWendtElsevier，1990：19～2511马洁，蒋雄．交流阻抗技术研究析氢反应动力学．应用化学（待发表）