Abstract
The initial process and mophology of electroless nickel played a domination role in adhesive strenghth of EN coating. The structure of initial deposits on certain matrixes was observed by TEM analysis. The deposition of a extremaly fine grain film depended on relative contrast between a coating and a matrix in crystal lattice parameters. When the coating and matrix had similar srystal lattice parameters. A extremely fine grain film was obtained. On the contrary, when the crystal lattice parameters were very different, a amorphous structure was observed.