Abstract
A molten carbonate fuel cell stack with an active area of 240 mm×140 mm consisted of 30 cells.The gas feed system works via interior manifolds,and the stack placed in a couple of self-chest,coupled with a heater at the bottom and other fours surrounded,to keep uniformity of temperature.Under ambient pressure and 650 ℃,fed with hydrogen and air as anode and cathode gases respectively,the stack gave a current density of 150 mA/cm 2 at an average cell voltage of 0.7 V.The peak output of the stack was 1.06 kW during its performance of 300 h.
Keywords
Molten Carbonate Fuel Cell(MCFC), Stack, Performance
Publication Date
2002-11-28
Online Available Date
2002-11-28
Revised Date
2002-11-28
Received Date
2002-11-28
Recommended Citation
Sheng SUI, Xin-jian ZHU, Zheng-yu FAN, CAO Guang-yi and.
Manufacture of 1 kW Molten Carbonate Fuel Cell Stack[J]. Journal of Electrochemistry,
2002
,
8(4): Article 17.
DOI: 10.61558/2993-074X.3311
Available at:
https://jelectrochem.xmu.edu.cn/journal/vol8/iss4/17
References
[1] AcresGJK .Recentadvancesinfuelcelltechnologyanditsapplication[J].JPowerSources,2001,100:60～66.
[2] DicksAndrew,SiddleAngie.Assessmentofcommercialprospectsofmoltencarbonatefuelcells[J].JPowerSources,2000,86:316～323.
[3] JansenD ,LaagPC ,OudhuisABJ,etal.Prospectsforadvancedcoal_fuelledfuelcellpowerplant[J].J .PowerSources,1994,49:151～165.
[4] JansenD ,MozaffarianM .Advancedfuelcellenergyconversionsystems[J].EnergyConversMagmt,1997,38(10_13):957～967.
[5] LunghiP ,UbertiniS ,DesideriU .Highlyefficientelectricitygenerationthroughahybridmoltencarbonatefuelcell_closedloopgasturbineplant[J].EnergyConversionandManagement,2001,42:1657～1672.
[6] HuijsmansJPP ,KraaijGJ ,MakkusRC ,etal.AnanalysisofenduranceissuesforMCFC[J].J .PowerSources,2000,86:117～121.
[7] PoresSJ,NesarajAS ,VadivelPR ,etal.Preparationofelectrolytematrixstructuresbyaqueousandnon_aque oustapecastingmethodformoltencarbonatefuelcells[J].BulletinofElectrochemistry,1999,15(9_10):400～403.
[8] HyunSH ,ChoSC ,ChoJY ,etal.Reinforcementofmoltencarbonatefuelcellmatrixesbyaddingrod_shapedγ_LiAlO2 particles[J].JMaterialsScience,2001,36:441～450.
Included in
Catalysis and Reaction Engineering Commons, Engineering Science and Materials Commons, Materials Chemistry Commons, Materials Science and Engineering Commons, Physical Chemistry Commons, Power and Energy Commons